Dynamically Vulcanized EPDM/PP (40/60) Blends

Dynamically vulcanized thermoplastic elastomer (TPE) blends were first described by Fisher. In the 1960s, the usage of TPE was low. However, the consumption of TPE is increasing today. Due to hard and soft polymer phases in its structure, TPE replaced a lot of materials. TPE materials are preferred today due to their good thermal properties, oxidation resistance, transparency, adhesion, compatibility with other polymers etc. As a result of the studies that were done in 1975, TPV—vulcanized thermoplastic elastomers were developed. In this study, TPV elastomers were produced by forming crosslinks with peroxide from different ratios, of EPDM and PP. Mixing was done with twin screw extruder. After that yield and tensile strength, the modulus of elasticity, % elongation, Izod impact strength, hardness, Melt Flow Index (MFI), Vicat Softening Point, Heat Deflection Temperature (HDT), and density of crosslinks were determined. Thermal transition temperatures and microstructure were determined with DSC and SEM, respectively.     

优力胶在注塑模具中的应用

对优力胶在双分型面、动定模碰穿、包胶模3种典型注塑模具结构中的应用进行了分析,阐述了优力胶在注塑模具中的适用场合及模具的运动原理,得出了优力胶在注塑模具结构设计中的技术要求和设计技巧,对模具设计者具有一定的借鉴。     

介电弹性体摆动驱动器的分析与实现

根据介电弹性体摆动驱动器的工作原理,设计了摆动驱动器.通过对比试验得到性能较佳的摆动驱动器,该摆动驱动器的研究可为仿生机器人的驱动实现提供一种可能的解决方案.     

反应型乳化剂在核壳丙烯酸酯乳液合成中的应用

本研究采用种子乳液聚合法,将反应型乳化剂、非离子型乳化剂和阴离子型乳化剂进行复配,以BA、St、MMA、AA为单体合成了具有核壳结构的聚丙烯酸酯类乳液。试验表明：乳化剂用量为2.5%,G-30∶NP40∶HAPS比例为1∶2∶1,乳化剂在核壳中的比例为2∶1,得到的乳液具有核壳结构,胶膜综合性能良好。     

多巴胺改性硅橡胶的制备及性能研究

通过硅氢化反应,在催化剂氯铂酸作用下,使聚氢基硅氧烷( PMHS)上的Si-H键与十一烯酸(UA)上的烯基发生加成,过量的Si-H键与聚烯基硅氧烷(PMVS)反应,合成了含羧基的十一烯酸-硅橡胶共聚物(UA-co-PDMS);接着利用UA-co-PDMS表面的羧基和多巴胺(DA)发生胺化反应,制得了多巴胺修饰的硅橡胶(...     

黑液-蒙脱土/聚氯乙烯/丁腈橡胶热塑性弹性体的制备及性能研究

采用蒙脱土对造纸黑液中的木质素进行絮凝沉淀,制备黑液-蒙脱土复合物(BL-MMT),然后将其应用于聚氯乙烯/丁腈橡胶(PVC/NBR)热塑性弹性体,并对其力学性能、耐老化性能及热降解性能进行测试。结果表明:随着BL-MMT中木质素蒙脱土比例增大,热塑性弹性体力学性能先增大后减小,适宜配比m(木质素)∶m(蒙脱土)=1∶1。BL-MMT份数增大,热塑性弹性体力学性能先增大后减小,20份时出现最大值。BL-MMT填充的PVC/NBR热塑性弹性体与添加炭黑和碳酸钙相比,力学性能和热性能相当,而耐老化性能更为优越。黑液-蒙脱土复合物可望用作PVC/NBR热塑性弹性体的补强剂。     

端羟基聚丙烯酸酯分子量对PUA性能的影响

异佛尔酮二异氰酸酯(IPDI)、聚己内酯二醇(PCL)为主要原料合成聚氨酯预聚体,甲基丙烯酸甲酯和丙烯酸丁酯合成端羟基共聚物,两者共聚并在水中分散,得到丙烯酸酯改性水性聚氨酯(PUA)。PUA乳液形貌表征结果表明,当聚丙烯酸酯数均分子量达到9 041时,复合乳液的稳定性变差;复合乳液平均粒径随聚丙烯酸酯(PA)分子量增大而增加,但都小于150 nm,并呈现典型的核壳结构。FTIR测试表明,随着PA链段分子量增大,其氢键相互作用相对减弱。DSC测试显示在PA分子量较低时,PA和PU链段是相容的。TG和拉伸测试结果显示,PUA的热稳定性及力学性能都得到明显改善。     

聚烯烃类热塑性弹性体研究进展

介绍了聚烯烃热塑性弹性体(TPO)的生产工艺、结构、性能及应用,叙述了乙烯-辛烯共聚物(POE)、热塑性动态硫化胶(TPV)和乙烯-辛烯(OBC)3种TPO的特点及应用领域.建议应对小型装置进行改造,提高产量,加大投入力度研发设计低耗能、低污染和高产量的大型装置;消化、吸收国外技术的同时加快创新力度;重点研发汽车、建筑...     

环氧树脂增韧改性研究进展

介绍了几种增韧改性环氧树脂的方法,包括互穿网络增韧、液晶聚合物增韧、核壳结构增韧、嵌段共聚物增韧及柔性固化剂增韧,分析了其机理,综述了上述改性方法的国内外研究进展。